Polypropylene Fibers 8529

According to major supplies, “Use of synthetic fibers for reinforcing concrete

is continuously, increasing. The increase has been considerable since 1980, but

slowed somewhat in 1990, a year of substantial construction cutbacks. Apparently

the construction community believes there are advantages in the use of synthetic

fibers in concrete.” (Schupack) Synthetic fibers are used to improve crack

control in concrete. Some reports say that synthetic fiber reinforced concrete (SFRC)

would replace welded wire fabric in many slab-on-grade applications. But in

reality if the welded wire fabric is placed properly it controls crack width

better than the synthetic fiber reinforced concrete. In a case study of the use

of synthetic fibers in reinforced concrete, the following conclusions were

obtained. No matter what concrete placing job is being done, there is no

substitute for good concrete practices. The use of a low fiber volume mix will

help control plastic shrinkage cracks and bleeding, but not give good cracking

control once the crack forms. The synthetic fibers running through a crack have

a poor bond providing no shear friction. Impact and toughness tests on synthetic

fiber reinforced concrete imply less edge spalling will occur. The American

Concrete Institute (ACI) conducted two studies on polypropylene fiber reinforced

concrete, one dealing with plastic shrinkage cracking and the other on

permeability characteristics. Plastic shrinkage cracking occurs when the surface

water on the concrete evaporates faster than the bleed water reaches the surface

of the concrete. It was determined by the plastic shrinking cracking study that

polypropylene fibers helped reduce the total plastic shrinkage crack area on

test panels. Also determined is that the screeding rate affects the total crack

area in polypropylene reinforced concrete, while finishing operations showed no

significant effects. This study also suggests the use of longer fibers (about

0.75in.) will produce less crack area. “Permeability plays an important role

in long-term durability of concrete materials. Permeability of concrete

generally refers to the rate at which particular aggressive substances (water,

sulfates, chloride ions, etc.) can flow through the concrete.” (Soroushian) As

discussed in the plastic shrinkage study that polypropylene fibers reduce

cracking. Less cracking in the concrete surface that surface would be less

permeable. In the permeability study, they concentrated on the effects of

chloride and the permeability of the concrete. The results of this study

concluded polypropylene fibers had little effects on chloride permeability of

concrete. The polypropylene fibers only help reduce plastic shrinkage cracks. In

residential construction, polypropylene fibers have been in use since the

mid-to-late 1970s. Polypropylene fibers are used for their high tensile strength

and low cost. These fibers fit into two categories, for early plastic shrinkage

and for improved long-term crack control. One of the first residential

applications of polypropylene fibers was in western Pennsylvania, in March of

1979. Fibers were used in all the flat work of the residence. Polypropylene

fibers have gained acceptance by residential home builders due to its

flexibility and its ability to conform to forms. Home builders say polypropylene

fibers help them sell more concrete by reducing the potential risks of cracking.

The use of polypropylene does not compensate for the lack of good design,

water/cement ratios, temperature and wind conditions. One important thing to

remember is nothing replaces good concrete practices.


Schupack, Morris, and William R. Stanley. “Seven Case Studies of Synthetic

Fiber Reinforced Slabs.” Concrete International Feb. 1992:50-56. Soroushian,

Parviz., Faiz Mirza, and Abdulraman Alhozaimy. “Permeability Characteristics

of Polypropylene Fiber Reinforced Concrete.” ACI Materials Journal

92(1995):291-295. Mirza, Faiz., Parviz Soroushian, and Abdulraman Alhozaimy.

“Plastic Shrinkage Cracking of Polypropylene Fiber Reinforced Concrete.” ACI

Materials Journal 92(1995):553-560. Biddle, Daniel T. “Fiber Reinforcement in

Residential Concrete.” Concrete International Feb. 1991:46-47.

Tagged In :

Get help with your homework

Haven't found the Essay You Want? Get your custom essay sample For Only $13.90/page

Sarah from studyhippoHi there, would you like to get such a paper? How about receiving a customized one?

Check it out